6.0mm²-Black/Red (H1Z2Z2-K)
(NO.7194003)– IEC 62930 / EN 50618:2014
■ General characteristics:
■ Application:
Specifically designed to connect photovoltaic system components inside and outside buildings
and facilities under high mechanical demands and extreme weather conditions.
■ Cable Construction:
Conductor
Material: Tinned annealed copper
Area(mm²): 1*6.0
Construction(N/mm): 84/0.285±0.005
Stranded diameter(mm): 3.016（Ref.)
Insulation: 125℃ XLPE Black
Nom. thickness (mm): 0.8 (Ref.)
Standard diameter (mm): 4.6±0.1
Jacket: 125℃ XLPE, Black / Red
Min. thickness (mm): 0.7
Nom. thickness (mm): 0.8 (Ref.)
Outer diameter (mm): 6.2±0.1
Making: ZION COMMUNICATION TÜV SÜD IEC62930
EN50618: 2014 H1Z2Z2-K 1×6.0mm² -40℃ to+90℃
DC 1500V HALOGEN FREE LOW SMOKE
■ Package:
100M/Roll, 500M/Wooden Drum
■ Electrical properties:
Nominal Voltage: H1Z2Z2-K: DC 1.5KV AC 1.0/1.0KV
Ambient Temperature: -40℃~+90℃
Max.Temperature at conductor: +125℃
Service life: ＞25 years ( -40℃~+90℃)
Voltage: 600/1000V
Temperature: -40~90℃
Conductor resistance (20℃): 3.39Ω/km
Insulation resistance (70℃): ≥1000 MΩ/km
Withstand voltage(V/5min): AC6500
Speak voltage(V/5min): AC6500
Min bending radius(mm): 4*D
■ The main performance parameter of finished cable:
Performance of Finished Cable
Voltage Test:
Min. Dipping Time in Water: ≥1 hour
Testing Voltage (AC): 6500V
Min. Voltage Applying Time: 5 min
Test Result: No breakdown
Sheath Surface Resistance:
Length of Specimen: 250mm
Test Result: ≥10⁹Ω
Insulation Resistance at 20℃:
Test Result: ≥10¹⁴Ω
High Temperature Stress (140℃):
Voltage Test (1.2V): No breakdown
Deep Pressure: Wall thickness reduced by 50%
Damp-Heat Resistance (90℃, 85% Humidity):
Tensile Strength Change: ≤30%
Elongation at Break Change: ≤-30%
Chemical & Mechanical Resistance
Acid-Alkali Resistance:
Dipping Time: 168 hours
Tensile Strength Change: ≤-30%
Elongation: ≥100%
Low-Temperature Bending (-40℃, 16h):
Test Result: No crack
Ozone Resistance:
Ozone Concentration: (200±50)×10⁻⁶
Test Time: 72 hours
Test Result: No crack
Heat Shrinkable Jacket Test:
Test Result: ≤2% Shrinkage
Flame Retardancy & Halogen Content
Flame Retardant – Vertical Burn Test:
Carbonization Length: ≥50mm
Downward Flame Spread: ≤540mm
Halogen Content (Non-Metallic Materials):
Chlorine & Bromine (HCl / HBr): ≤0.5%
Fluoride (F): ≤0.1%
Mechanical Properties of Insulation & Sheath
Before Aging:
Tensile Strength: 8.0 N/mm²
Elongation: 125%
After Aging:
Tensile Strength Change: ≤-30%
Elongation at Break Change: ≤-30%
Hot Extension (200℃):
Elongation Under Load: ≤100%
Elongation After Unloading: ≤25%